        Anti PID series EVA film

        F406P&F806P


        Product introduction 

        The Potential Induced Degradation (PID) within the system of a solar module may cause severe power loss of PV system. F?RST? F406P&F806P EVA provides an encapsulant solution for a PID-free requirement of the PV module. F?RST? F406P&F806P EVA provides excellent PID-resistance which can withstand 96h PID testing under conditions of 85℃, RH 85%, -1000Vdc. The P-series EVA also exhibits excellent durability and high transmittance.


        Anti PID property (85℃,85%RH,-1000Vdc)

        Glass + F406P EVA + Silicon cell+ F806P EVA + BEC301 Backsheet

              Initial(251.2W)                    PID96h(250.6W)

              


        Performance parameter

        Properties Test Method Units F406P F806P
        General gram weight FST Method g/m2 430±20 390±20
        Thickness  FST Method mm 0.55±0.05 0.50±0.05
        Length FST Method m/roll 150 150
        Width FST Method mm Customization0/+7 Customization0/+7
        Density ASTMD792 g/cm3 0.95-0.96 0.95-0.96
        Melting range FST Method 40-80 40-80
        Shrinkage Rate(120,3min) GB/T29848 MD% <3.0 <3.0
        TD% <1.5 <1.5
        UV-Cutoff Wavelength FST Method nm -- 360
        Transmittance 1100nm-380nm GB/T29848 % >91 >91
        380nm-290nm % >80 <30
        Gel content GB/T29848 Gel% >75 >75
        Volume Resistivity GB/T29848 Ω·cm >1.0×1015 >1.0×1015
        Strength of Peeling from Glass GB/T29848 N/cm >60 >60
        Strength of Peeling from TPT GB/T29848 N/cm >40 >40
        Note: The gram weight, thickness, length and width of product can be customized.